Application of cas: 38103-06-9 | Kolesnikov, Timofey I. et al. published an article in 2021

5,5′-((Propane-2,2-diylbis(4,1-phenylene))bis(oxy))bis(isobenzofuran-1,3-dione)(cas: 38103-06-9) is a diallyl based epoxy modification agent that blends with the resin to improve the mechanical property of the epoxy material.Computed Properties of C31H20O8 It is majorly used in novalac based resins, which can be further cured with bismaleimides (BMI) for aerospace, electronics and wireless communication based applications.

Computed Properties of C31H20O8《Dual-curing propargyl-phthalonitrile imide-based thermoset: Synthesis, characterization and curing behavior》 was published in 2021. The authors were Kolesnikov, Timofey I.;Orlova, Alexandra M.;Tsegelskaya, Anna Y.;Cherkaev, Georgij V.;Kechekyan, Alexander S.;Buzin, Alexander I.;Dmitryakov, Petr V.;Belousov, Sergey I.;Abramov, Igor G.;Serushkina, Olga V.;Kuznetsov, Alexander A., and the article was included in《European Polymer Journal》. The author mentioned the following in the article:

Oligoimide containing propargyl and phthalonitrile groups in one mol. (OI-PR-PN) was synthesized by a facile and eco-friendly method in benzoic acid melt. To incorporate side propargyl groups into the polyimide backbone, a new monomer was developed – 5-(2-propyn-1-yloxy) benzene-1,3-diamine (PBD). The OI-PR-PN dual-curing behavior was studied by DSC and FT-IR methods. The curing of phthalonitrile groups can be promoted by the intermediates formed during the propargyl groups polymerization This allows crosslinking of phthalonitrile groups at 300-350°C in one component system. OI-PR-PN showed good solubility in low b.p. solvents and had low melt viscosity (up to 8 Pas at 250°C). The temperatures of 10% weight loss of the cross-linked OI-PR-PN and oligoimide containing only propargyl groups (OI-PR) are 496°C and 450°C correspondingly. The completely cured OI-PR-PN glass transition temperature measured by dynamic mech. anal. was 424°C with a storage modulus 4.2 GPa at 50°C. The possibility of crosslinking without using curing additives with a combination of excellent thermal and mech. properties indicates the potential of OI-PR-PN as a matrix for composite manufacturing To complete the study, the researchers used 5,5′-((Propane-2,2-diylbis(4,1-phenylene))bis(oxy))bis(isobenzofuran-1,3-dione) (cas: 38103-06-9) .

5,5′-((Propane-2,2-diylbis(4,1-phenylene))bis(oxy))bis(isobenzofuran-1,3-dione)(cas: 38103-06-9) is a diallyl based epoxy modification agent that blends with the resin to improve the mechanical property of the epoxy material.Computed Properties of C31H20O8 It is majorly used in novalac based resins, which can be further cured with bismaleimides (BMI) for aerospace, electronics and wireless communication based applications.

Reference:
Benzofuran – Wikipedia,
Benzofuran | C8H6O – PubChem